ShangHai Weizhen Industrial CO.,LTD Provide Best Epoxy Resin Worktops to Your Laboratory Solution
Add to Cart
Epoxy Resin Undermount Sink For Laboratory Furniture With Different Color
Descirption:
Except supply epoxy resin worktops, epoxy sink is also one of our products. It is drop-in style sinks, and convenient for user to install and clean spill water. The sinks are top mounted into a recessed cutout eliminating the need for undermount sink support systems. It is not easy to gather the residual chemicals and bacteria.
Specification:
| Physical Test Results | |||
| No. | Test Item | Test Method | Result |
| 1 | Compressive Test | ASTM D695-10 | 24000psi |
| 2 | Deflection Temperature Under Load | ASTM D648-07 Method B | 262℃ |
| 3 | Density | ASTM D792-13 Method B | 133.8lb/ft3 |
| 4 | Flexural Strength | ASTM D790-10 Method A | 12200psi |
| Flexural Modulus | 2350000psi | ||
| 5 | Horizontal Burning | ASTM D635-10 | Classification:HB |
| 6 | Rockwell Hardness | ASTM D785-08 Procudure A | HRM98.3 |
| 7 | Water Absorption | ASTM D750-98(2010)e1 | 0.031% |
| 8 | High Temperature Resistance Test | _ | No bubbles,rupture,deformation on the surface |
| 9 | Fire Resistatnce Test | _ | No bubbles,rupture,crack on the surface |
Repair Scratch:
It’s repairable and without any trace when the surface was been damaged, of course, it won’t affect chemical and physical properties. Mild scratches can be removed by non-woven with oil, and then cleaned by a dry cloth. Deeply scratches can be polished with water sandpaper along with the scratches until it disappear, and can also be polished by polishing machine. The strength should be as small as possible to get the better repair effect, and finally use non-woven dampened with oil clean the grinding place, followed by using a clean cloth.
Mild Scratches
Wiping along with scratches by non-woven with maintain oil repeatedly until scratches disappeared, and then cleaned by dry cloth.
Deeply Scratches
Wiping along with scratches by different meshes wet sandpaper, 800 grit~2000 girt is suggested. Depend on the depth of scratch, using coarse sandpaper polish scratch firstly, then polishing it by sandpaper or polish machine with slightly strength, and finally use non-woven dampened with oil clean the grinding place, followed by using a clean cloth.